同步活化磁化制备磁性多孔炭去除水中孔雀石绿
|
苏石川,林立涛,王亮
|
Magnetic porous carbon prepared by synchronous activation magnetization to remove malachite green from water
|
Shichuan SU,Litao LIN,Liang WANG
|
|
表1 磁性多孔炭的基本理化性质
|
Table 1 Basic parameters for the magnetic porous carbon composites
|
|
样品 | C质量分数/% | H质量分数/% | N质量分数/% | 比表面积/(m2·g-1)a | 微孔比表面积/(m2·g-1)b | 微孔率/% | 孔容/(cm3·g-1) | MC-0-Fe | 74.5 | 1.64 | 0.34 | 1 389 | 1 024 | 73.8 | 0.768 | MC-0.01-Fe | 84.4 | 1.69 | 0.43 | 1 614 | 1 209 | 74.9 | 0.854 | MC-0.02-Fe | 83.4 | 1.51 | 0.38 | 1 885 | 1 385 | 73.5 | 1.032 | MC-0.04-Fe | 75.8 | 1.38 | 0.36 | 1 797 | 1 330 | 74.0 | 1.009 | MC-0-Zn | 62.3 | 1.73 | 0.11 | 458.3 | 182.6 | 39.8 | 0.358 | MC-1/2-Zn | 78.6 | 2.00 | 0.28 | 1 435 | 1 086 | 75.7 | 0.794 | MC-1/1-Zn | 84.1 | 1.51 | 0.52 | 2 302 | 1 834 | 79.7 | 1.176 | MC-2/1-Zn | 78.9 | 1.31 | 0.54 | 2 024 | 118.2 | 5.83 | 1.314 |
|
|
|