磁处理对碳酸钙过饱和溶液析晶影响的TLVM研究

展开
  • 同济大学物理系环境物理研究室, 上海 200092
朱国栋(1978- ),同济大学物理系环境物理研究室在读 博士研究员。电话:021--65982253,E-mail:epspm@mail. tongji.edu.cn。

收稿日期: 2004-07-18

  网络出版日期: 2010-10-01

基金资助

国家自然科学基金资助项目,项目号:59738150

Effect of the magnetic treatment on the crystals precipitated frOm thesupersaturated calcium carbonate solution:a TLVM study

Expand
  • Environment Research Group, Physics Department, Tongji University, Shanghai 200092, China

Received date: 2004-07-18

  Online published: 2010-10-01

摘要

利用时间延迟摄像显微镜(TLVM)系统,研究了磁处理对碳酸钙过饱和溶液析出晶型的影响。结果表明,磁处理增加了溶液中文石生成的几率,沉淀中文石浓度增多,方解石成分减少。在整个TLVM实时观测过程中,未发现任何的晶型间的转变。流速对磁处理效果影响的研究表明,存在最佳流速,在该流速下,过饱和溶液析出物中几乎全为文石和少量的球霰石,而没有方解石的成分,从而形成软垢,达到最佳的阻垢效果。

关键词: 磁处理; 方解石; 文石; 流速

本文引用格式

朱国栋, 徐敬, 李陈, 蔺磊, 李杰 . 磁处理对碳酸钙过饱和溶液析晶影响的TLVM研究[J]. 工业水处理, 2005 , 25(3) : 52 -55 . DOI: 10.11894/1005-829x.2005.25(3).52

Abstract

Using time lapse video microscope system, the efect of magnetic treatment on the deposits precipitated from the supersaturated calcium carbonate solution has been studied. e results show that magnetic treatment increases the possibility of aragonite growing from solutions,and,when compared with the untreated ones,preci—pitats consists of more aragonite crystals and fewer calcite after the solutions are magnetically treated.During the whole experimental process,no chan ges between diferent crystal phases could be observe&There exists an optimum flow rate, within which the depo sits could be composed mostly of aragonite and a few vaterite crystals. These “soft”scales could be easily removed.So,at this velocity,magnetic treatment could have the best antiscale efect.

参考文献

[1] Vemeiren T. Magnetic treatment device for liquids [P]. US 2652925,1953.
[2] Baker J S, Judd S J. Magnetic amelioration of scale formation [J].Wat. Res., 1996, (2) :247 -260.
[3] Dalas E, Koutsoukos P G. The effect of magnetic fields on calcium carbonate scale formation [J]. J. Cryst. Growth, 1989,96: 802-806.
[4] Gabrielli C, et al. Magnetic water treatment for scale prevention[J].Wat. Res., 2001,35:3 249-3 259.
[5] Grimes C. Magnetic field effect on crystals[J]. Tube Int., 1988,(3):111-118.
[6] Higashitani K, et al. Effects of magnetic field on formation of CaCO3paticles[J]. J. Coll. Int. Sci., 1993,156:90-95.
[7] 林艺辉,方键,李杰.磁场对碳酸钙析晶过程影响的定量研究[J].工业水处理,2002,22(6):16-18.
[8] Gehr R, et al. Reduction of soluble mineral concentrations in CaSO4saturated water using a magnetic field[J]. Wat. Res., 1995,29:933-940.
[9] Busch K W, et al. Studies of a water treatment device that uses magnetic fields[J]. Corrosion, 1986,(42):211-221.
[10] Donaldson J D. The magnetic treatment of fluids [J]. Brewers'Guardian, 1990, (7) :20-24.
[11] Parsons S A, et al. Magnetically augmented water treatment [J].Trans. IChemE, 1997,75B :98-104.
[12] Cobe S, et al. Nucleation and crystallization of CaCO3 in applied magnetic fields [J]. Crystal Engineering, 2002, (5) :243-253.
[13] Ellingsen. Proc. 14th World Congr. Int. Wat. Suppl. Assoc. [C].Zuich, SS8, 1982. 12-25.
[14] 谢伟明,等.磁化水阻垢技术研究[J].水处理技术,1990,(2):1-5

文章导航

/