Corrosion of power plant’s copper tubes on different water quality conditions

Expand
  • Industrial Chemistry Institute, Nanjing University of Science & Technology, Nanjing 210094, China

Received date: 2005-09-07

  Revised date: 2005-09-07

  Online published: 2010-10-01

摘要

电厂铜材的腐蚀问题日益突出,引起铜腐蚀的原因是多方面的,其中水质工况是非常重要的因素之一。从水中主要阴离子、阻垢剂、缓蚀剂、微生物生长等方面探讨了不同水质工况下铜管的腐蚀作用。

关键词: 铜管; 凝汽器; 循环水; 腐蚀

本文引用格式

夏明珠, 雷武, 王风云 . 不同水质工况下电厂铜管的腐蚀[J]. 工业水处理, 2006 , 26(1) : 46 -48 . DOI: 10.11894/1005-829x.2006年.26(01).46

Abstract

Copper corrosion in power plants is becoming obviously a severe problem, the causes involve in many aspects. Water quality condition is a very important factor. The corrosion of copper tube on different water quality conditions are discussed on several aspects, including the main anions in water, scale inhibitors and corrosion inhibitors added into water, microorganisms growth, etc.

参考文献

[1] 梁磊, 吴一平, 周国定. 电厂凝汽器冷却管腐蚀及泄漏情况调查[J]. 电站辅机, 1998(3) : 6-8.
[2] 朱志平, 杨道武. 凝汽器铜管的联合保护研究[J]. 热能工程, 2003(1): 89-94.
[3] 苏光浩, 舒保华. 发电厂凝汽器铜管的腐蚀[J]. 发电设备, 2000 (1) : 20-23.
[4] 曹杰玉, 龙国军, 汪德良, 等. 残 C 膜对凝汽器黄铜管早期腐蚀穿 孔影响的研究[J]. 热力发电, 2002(6) : 64-67.
[5] 杨欲明. 火电厂汽轮机凝汽器的腐蚀与防护[J]. 电力情报, 1998 (1):34-36.
[6] 窦照英. 凝汽器管腐蚀及处理实例[J]. 华北电力技术,1998(10):30-33.

文章导航

/