600 MW机组凝汽器不锈钢管腐蚀原因分析
常亮,王锋涛,张小霓,王卫军,薛昌刚,王超煜
Analysis on the corrosion causes of stainless steel tubes in condensers of 600 MW unit
Liang Chang,Fengtao Wang,Xiaoni Zhang,Weijun Wang,Changgang Xue,Chaoyu Wang
表7
管样3汽侧蚀坑处物质的能谱分析结果
%
元素
O
Na
Cl
Si
Ca
Fe
Cr
S
Ni
Mo
EDS Spot 1
28.93
18.70
12.85
1.68
3.25
21.6
2.97
2.31
1.02
—
EDS Spot 4
46.71
15.52
3.13
2.89
2.26
23.96
0.89
—
0.34
2.11
EDS Spot 5
22.89
8.58
1.61
2.02
2.34
51.28
5.25
—
3.07
0.97