含锑废水深度处理技术研究与中试示范

doi:10.19965/j.cnki.iwt.2023-0042

摘要/Abstract

摘要：

以某锑制品厂混凝沉淀处理后的低浓度含锑废水为吸附对象，在小试中通过单因素实验得到最佳吸附条件，再通过动态化吸附和再生实验确定深度处理磁分离技术的最佳工艺参数。该技术使出水的锑质量浓度能稳定达到排放标准（5 μg/L）。小试结果表明，在铁基Fenton改性磁性吸附剂（AFS350）投加2.0 g/L，吸附1.0 h，搅拌速度200 r/min的条件下，出水锑的质量浓度降为0.004 mg/L。中试结果表明，AFS350投加3 g/L，搅拌速度300 r/min，吸附2.0 h后，锑的去除率高达98.91%。此工艺技术实现了磁性吸附材料全自动分离回收及再生利用，同时具有较高的经济效益和可持续发展的潜力，为工业含锑废水的深度处理提供了一种可行方案。

关键词: 水处理技术, 磁性吸附材料, 含锑废水

Abstract:

The low concentration antimony-containing wastewater from an antimony product plant after coagulation and precipitation treatment was used as the adsorption object，and the optimal adsorption conditions were obtained by single-factor experiments. Then，the optimal process parameters of the magnetic separation technology for deep treatment were determined by dynamicized adsorption and regeneration experiments. The technology enabled the effluent antimony mass concentration to reach the discharge standard（5 μg/L） stably. The results of the experiments showed that the mass concentration of antimony was reduced to 0.004 mg/L under the conditions of iron-based Fenton-modified magnetic adsorbent（AFS350） dosing of 2.0 g/L，adsorption for 1.0 h and stirring speed of 200 r/min. The results of the pilot test showed that the removal rate of antimony after AFS350 dosing of 3 g/L，stirring speed of 300 r/min and adsorption for 2.0 h was up to 98.91%. This process technology achieves fully automatic separation and recovery and recycling of magnetic adsorption materials，and at the same time had high economic efficiency and sustainable development potential，providing a feasible solution for the deep treatment of industrial antimony-containing wastewater.

Key words: water treatment technology, magnetic adsorption material, antimony-containing wastewater

中图分类号:

X703

陈韬, 付广义, 钟宇, 李琼花, 田石强, 成应向. 含锑废水深度处理技术研究与中试示范[J]. 工业水处理, 2023, 43(8): 179-184.

Tao CHEN, Guangyi FU, Yu ZHONG, Qionghua LI, Shiqiang TIAN, Yingxiang CHENG. Research and pilot-scale demonstration of advanced treatment technology for antimony-containing wastewater[J]. Industrial Water Treatment, 2023, 43(8): 179-184.

https://www.iwt.cn/CN/Y2023/V43/I8/179

图/表 9

参考文献 15

1	LONG Xiaojing， WANG Xin， GUO Xuejun，et al. A review of removal technology for antimony in aqueous solution［J］. Journal of Environmental Sciences，2020，90：189-204. doi:10.1016/j.jes.2019.12.008
2	ZHANG Chuanqiao， WU Mingyang， WU Kun，et al. Efficient removal of antimonate and antimonite by a novel lanthanum-Manganese binary oxide：Performance and mechanism［J］. Journal of Hazardous Materials，2023，442：130132. doi:10.1016/j.jhazmat.2022.130132
3	UNGUREANU G， SANTOS S， BOAVENTURA R，et al. Arsenic and antimony in water and wastewater：Overview of removal techniques with special reference to latest advances in adsorption［J］. Journal of Environmental Management，2015，151：326-342. doi:10.1016/j.jenvman.2014.12.051
4	DAUD M K， NAFEES M，ALI S，et al. Drinking water quality status and contamination in Pakistan［J］. Biomed Research International，2017：1-18. doi:10.1155/2017/7908183
5	GUO Wenjing， FU Zhiyou， WANG Hao，et al. Removal of antimonate（Sb（Ⅴ）） and antimonite（Sb（Ⅲ）） from aqueous solutions by coagulation-flocculation-sedimentation（CFS）：Dependence on influencing factors and insights into removal mechanisms［J］. Science of the Total Environment，2018，644：1277-1285. doi:10.1016/j.scitotenv.2018.07.034
6	LI Guifa， ZHAO Pengsen， ZHENG Haizhong，et al. Research on the removal mechanism of antimony on α-MnO₂ nanorod in aqueous solution：DFT+U method［J］. Journal of Hazardous Materials，2018，354：8-16. doi:10.1016/j.jhazmat.2018.04.055
7	NARIMANI-SABEGH S， NOROOZIAN E. Magnetic solid-phase extraction and determination of ultra-trace amounts of antimony in aqueous solutions using maghemite nanoparticles［J］. Food Chemistry，2019，287：382-389. doi:10.1016/j.foodchem.2019.02.112
8	MA Baiwen， WANG Xing， LIU Ruiping，et al. Synergistic process using Fe hydrolytic flocs and ultrafiltration membrane for enhanced antimony（Ⅴ） removal［J］. Journal of Membrane Science，2017，537：93-100. doi:10.1016/j.memsci.2017.05.022
9	SUN Weimin， XIAO Enzong， KALIN M，et al. Remediation of antimony-rich mine waters：Assessment of antimony removal and shifts in the microbial community of an onsite field-scale bioreactor［J］. Environmental Pollution，2016，215：213-222. doi:10.1016/j.envpol.2016.05.008
10	MIAO Yangyang， HAN Feichao， PAN Bingcai，et al. Antimony（Ⅴ） removal from water by hydrated ferric oxides supported by calcite sand and polymeric anion exchanger［J］. Journal of Environmental Sciences，2014，26（2）：307-314. doi:10.1016/s1001-0742(13)60418-0
11	CHITHAMBARA THANU V R， JAYAKUMAR M. Electrochemical recovery of antimony and bismuth from spent electrolytes［J］. Separation and Purification Technology，2020，235：116169. doi:10.1016/j.seppur.2019.116169
12	连晓燕，王东田，钟宇，等. 混凝法处理工业含锑废水研究进展［J/OL］.工业水处理.
	LIAN Xiaoyan， WANG Dongtian， ZHONG Yu，et al. Research progress on the treatment of industrial antimony-containing wastewater by coagulation［J/OL］.Industrial Water Treatment，2022：1-17. Doi：10.19965/j.cnki.iwt.2022-0717 .
13	苏文龙，成应向，陈韬，等. 芬顿污泥制备磁性吸附剂去除水中Sb（Ⅴ）［J］. 环境工程学报，2022，16（7）：2165-2177. doi:10.12030/j.cjee.202202014
	SU Wenlong， CHENG Yingxiang， CHEN Tao，et al. Preparation of Fenton sludge-based magnetic adsorbent for Sb（Ⅴ） removal from water［J］. Chinese Journal of Environmental Engineering，2022，16（7）：2165-2177. doi:10.12030/j.cjee.202202014
14	INAM M ALI， KHAN R， YEOM I T，et al. Optimization of antimony removal by coagulation-flocculation-sedimentation process using response surface methodology［J］. Processes，2021，9（1）：117. doi:10.3390/pr9010117
15	WANG Xiangqin， HE Mengchang， LIN Chunye，et al. Antimony（Ⅲ） oxidation and antimony（Ⅴ） adsorption reactions on synthetic manganite［J］. Geochemistry，2012，72：41-47. doi:10.1016/j.chemer.2012.02.002

名称	功率/kW	处理成本/（元·kg^-1）	备注
合计		1.029	电费按0.6元/（kW·h）计算
鼓风干燥箱	1.7	0.043	容积126 L
粉碎机	3	0.112	尺寸608 mm×600 mm×745 mm
球磨机	0.55	0.041	磨样量8 kg
管式炉	3	0.675	加热有效容积8 L
硫酸	—	0.018	稀释后对煅烧产物改性
恒温水浴锅	1.5	0.112	尺寸940 mm×170 mm×90 mm
真空干燥箱	1.5	0.028	尺寸715 mm×530 mm×1 200 mm

名称	功率/kW	处理成本/（元·kg^-1）	备注
合计		1.029	电费按0.6元/（kW·h）计算
鼓风干燥箱	1.7	0.043	容积126 L
粉碎机	3	0.112	尺寸608 mm×600 mm×745 mm
球磨机	0.55	0.041	磨样量8 kg
管式炉	3	0.675	加热有效容积8 L
硫酸	—	0.018	稀释后对煅烧产物改性
恒温水浴锅	1.5	0.112	尺寸940 mm×170 mm×90 mm
真空干燥箱	1.5	0.028	尺寸715 mm×530 mm×1 200 mm

技术难点	解决方法
吸附剂的选择	提出解决Fenton污泥有效处置的方法，贯彻“以废治废”的绿色环保理念，并实现再生利用是整个工艺技术的特色之一，所以采用铁基Fenton改性磁性吸附剂
磁分离工艺	吸附技术已有广泛的工程技术应用，基于节约资源降低成本的目的，只需要在场内搭建磁分离处理系统，经初步计算，结合规模效应以及磁性材料回收，磁分离工艺深度处理含锑废水成本有望低于1元/t，相较于其他深度处理工艺，具有一定的成本优势，可操作性强
吸附剂的再生性能	AFS350吸附剂再生后的吸附容量会受损，影响后续的锑去除率，运行过程中需添加新吸附剂与再生后的吸附剂混合使用。后续可以重点研究Fenton污泥改性后的磁性吸附剂本身的性能提升，优化再生条件，磁性吸附材料的回收可产生可观的经济效益

技术难点	解决方法
吸附剂的选择	提出解决Fenton污泥有效处置的方法，贯彻“以废治废”的绿色环保理念，并实现再生利用是整个工艺技术的特色之一，所以采用铁基Fenton改性磁性吸附剂
磁分离工艺	吸附技术已有广泛的工程技术应用，基于节约资源降低成本的目的，只需要在场内搭建磁分离处理系统，经初步计算，结合规模效应以及磁性材料回收，磁分离工艺深度处理含锑废水成本有望低于1元/t，相较于其他深度处理工艺，具有一定的成本优势，可操作性强
吸附剂的再生性能	AFS350吸附剂再生后的吸附容量会受损，影响后续的锑去除率，运行过程中需添加新吸附剂与再生后的吸附剂混合使用。后续可以重点研究Fenton污泥改性后的磁性吸附剂本身的性能提升，优化再生条件，磁性吸附材料的回收可产生可观的经济效益

[1]	赵泽津, 熊久强. 文献计量学分析养殖业废水处理技术研究现状[J]. 工业水处理, 2024, 44(6): 69-77.
[2]	霍荣帆, 张瀚文, 刘垒, 何文文, 陈正军. 硝基芳香化合物废水处理技术研究进展[J]. 工业水处理, 2023, 43(2): 33-42.
[3]	连晓燕, 王东田, 钟宇, 魏杰. 混凝法处理工业含锑废水研究进展[J]. 工业水处理, 2023, 43(10): 53-62.
[4]	李志萍, 杨晶晶, 孙程奇, 白仁碧. 水中锑污染处理方法的研究进展[J]. 工业水处理, 2018, 38(6): 12-16,26.
[5]	沈建华, 肖才林, 张永威, 韩法昌, 李甫昌, 李睿华. 发制品废水处理技术研究进展[J]. 工业水处理, 2016, 36(11): 5-9.
[6]	陈宝银, 王少坡, 于静洁, 邱春生, 范志云, 孙力平. 水中内分泌干扰物去除技术研究进展[J]. 工业水处理, 2013, 33(7): 1-4.
[7]	李珍珍, 罗建中, 马莉娜, 谭广添, 林伟成. 工业园印染污水中重金属识别与集中处理技术研究[J]. 工业水处理, 2013, 33(2): 9-12.
[8]	魏芳芳, 张以河, 吕凤柱. TNT红水处理技术[J]. 工业水处理, 2012, 32(6): 11-15.
[9]	刘澜, 郑怀礼, 沈烈翔, 蒋绍阶, 张会琴. 不同给水处理工艺对饮用水生物稳定性的影响[J]. 工业水处理, 2010, 30(3): 9-12.
[10]	杨璋, 杨文忠. 南京工业大学水处理技术的发展回顾[J]. 工业水处理, 2010, 30(12): 3-5,41.
[11]	刘魁元. 献给《工业水处理》创刊30年[J]. 工业水处理, 2010, 30(12): 1-2.
[12]	潘碌亭, 吴锦峰. 聚合硫酸铁制备技术的研究与进展[J]. 工业水处理, 2009, 29(9): 1-5.
[13]	谢治民, 陈镇, 刘唐贵, 戴友芝. 铁改性海泡石除锑影响因素及再生研究[J]. 工业水处理, 2009, 29(11): 35-38,79.
[14]	陈进生. 发电机内冷水水质调控处理技术[J]. 工业水处理, 2005, 25(10): 14-17.
[15]	明云峰. IONPURE,大力开拓中国EDI市场[J]. 工业水处理, 2005, 25(1): 77-78.

选择文件类型/文献管理软件名称

选择包含的内容